温度サイクルチャンバーと温度ショックを簡単に見てみましょう

これまでのところ、温度衝撃試験と温度サイクル試験の用途は似ていると考える人はまだたくさんいますが、人々は2つの試験装置の違いについて十分に知らず、同じ試験と見なすことさえあります。 それならあなたは間違っています。
温度衝撃
温度衝撃 test, known as high and low temperature shock test, cold and thermal impact test, is used to test the degree of material structure or composite material that can be tolerated under the continuous environment of extremely high temperature and extremely low temperature in an instant, so as to test chemical changes or physical damage caused by thermal expansion or contraction in a short time. The temperature impact test chamber has a temperature change rate greater than 10 degrees/minute, and the heating/cooling rate is not less than 30C/ minute. The temperature change range is large, and the test severity also increases with the increase of the temperature change rate

温度サイクル試験

温度サイクル試験 is also known as thermal cycle test, high and low temperature cycle test, that is, the test sample is exposed to a preset high and low temperature alternating test environment. In order to avoid the impact of temperature shock, the temperature change rate during the test must be less than 20℃/ min. At the same time, in order to achieve the effect of creep and fatigue damage, it is recommended that the test temperature cycle is 25℃~100℃, or it can also use a cycle test of 0℃~100℃ according to the use of the product, and the exposure time is 15 minutes.

The difference between temperature impact test chamber and Temperature cycling chamber is mainly due to the different stress loading mechanism. The temperature shock test mainly examines the failure caused by creep and fatigue damage, while the Temperature cycling test mainly examines the failure caused by shear fatigue. 温度衝撃 test allows the use of two tank test equipment; The temperature cycle test was carried out with a single tank test device. The temperature change rate in the second tank should be greater than 50 ° C /min. Therefore, the most fundamental difference between the Temperature cycling test and the temperature shock test is that the temperature conversion is carried out at a constant rate
通常の状況では、変化率が5°C/minを超える場合は、急速温度変化試験と見なすことができます。温度衝撃とは、指定された時間内に高温領域と低温領域の交換を実現することです。一般的な試験方法では、温度ゾーンの切り替え時間は20秒以内である必要があります。試験室の出口温度は5分以内に安定させ、サンプル温度は15分以内に安定させることができます。低温、高温、高温多湿、低温低湿などの複雑な自然環境を正確にシミュレートできます。プラスチック、電子機器、食品、衣類、車両、金属、化学薬品、建築材料、その他の産業の信頼性試験に適しています。
温度サイクル試験室は、試験前後のゴムとプラスチックの材料変化と強い減衰低減度を比較するために、高温高湿環境を提供できます。また、コンテナ環境をシミュレートして、高温多湿下でのゴムやプラスチックの色あせや収縮を検出することもできます。
この装置は、さまざまな材料の耐熱性、耐寒性、耐湿性をテストするように設計されています。
温度衝撃は、主に炉の熱試験やバッテリーの安全性能試験の加熱試験に使用されますが、温度サイクル試験室と比較して、温度衝撃試験室には湿度がありません。